Passivation of stainless steel

Passivation is a finishing process for stainless steel and other metals. By removing free iron and thus increasing the chromium content in the metal, passivation improves the natural corrosion resistance of stainless steel.

What is passivation?

Passivation is a finishing process for stainless steel and other metal workpieces. Passivation is a non-electrolytic chemical procedure which creates an outer layer of shield material. It removes free iron from the surface through the application of nitric acid or citric acid. Thus, the steel parts are less likely to react with air and therefore show better corrosion resistance

As a consequence of removing free iron and therefore increasing the chromium content in the metal, the passivation process achieves a thicker chromium oxide layer. This results in a significantly improved corrosion resistance of steel and other metals.

Why should stainless steel grades get passivated?

Stainless steel naturally show great corrosion resistance. However, it is not completely immune to corrosion, especially rust. Stainless steel owes the great corrosion resistance to the high chromium content in the alloy. Due to the chemical reaction of chromium and oxygen, stainless steel forms a protective thin layer of chromium oxide on the surface. However, in spite of the oxide layer small spots on the surface may begin to rust. This happens because water molecules, due to grain boundaries or foreign matter, are able to oxidize some of the iron in the spots. This process is called rouging.

The removal of the contaminants and the oxide growth process is called passivation.

How does passivation work?

There are several specifications for the passivation process of steel and other metals, depending on the different standards (ASTM A967, AMS2700, ASTM A380). Mostly, the different passivation standards have some steps in common. First, the steel gets cleaned from foreign materials and particles of iron. Second, the workpiece gets chemical treatment via immersion. This step takes place in acid bath, usually nitric or citric acid. And finally, the stainless steel surface gets tested whether the chemical treatment was successful.

The procedure of passivation accelerates the natural process which occurs when the material is exposed to oxygen in the atmosphere. Thus, it helps to build the inert, oxide layer in a quicker way. Further, the build-up protective layer becomes significantly thicker than found in nature.

The process of passivation in detail

As already mentioned, all different passivation specifications have following steps in common. The first step in the passivation procedure is cleaning of the workpiece. The steel must be perfectly clean of any contaminants. This circumstance is proven by a validating test. After the cleaning, the parts are placed in an acidic passivating bath. Depending on the stainless steel grade, one of these approaches can be used — nitric acid passivation, nitric acid with sodium dichromate passivation and citric acid passivation. The duration, which usually has a minimum of 20 to 30 minutes, and the temperature, which ranges from ambient to 60° C, of the passivation process are predetermined. Next, the parts are neutralized through a bath aqueous sodium hydroxide. Finally, the steel workpiece gets rinsed with clean water and dried. To validate the results of the passivation process, the surface undergoes a testing procedure with humidity, elevated temperature or with salt spray.

Martensitic stainless steel, however, must receive a special treatment due to it is difficult to passivate.

How to further improve wear resistance

In certain application areas, the natural passivation may not suffice to protect the material from corrosion and wear. In these cases, BorTec provides the perfect solution. The EKABOR® technology increases the wear protection of unalloyed and low alloyed steels through boriding. Further, Borocoat® diffusion layers increase the layer hardness and improve the resistance of adhesive and abrasive wear of steel. For further information about our products, don’t hesitate to contact us!

To the Overview
Beitrag teilen
Our service for you
  • Technical consulting for solving your wear challenges.
  • Boronizing (boriding) with our BOROCOAT® technology and process development.
  • Subsequent heat treatments such as vacuum hardening and tempering.
  • Metallographic examinations
  • Providing of EKABOR® boronizing agents
Our Team

As a privately owned company with long term experience in the boronizing market our team is dedicated helping you being successful with your boriding solution.Trust in our technical expertise and competent sales team!

Büroleiterin
Jennifer Hassenrück
+49 2233 406-301
+49 2233 406-333
j.hassenrueck@bortec.de
Nordamerika
Drew Hogan
+1 (403) 464 0595
d.hogan@bortec-na.com